|Reinforcement:||Polyester Fabric/Fiberglass Fabric||Finish:||Black PE Film/Aluminum Foil/Sand/Mineral|
roof membrane under shingles,
asphalt roof membrane
Black PE Film Finish SBS Waterproof Membrane for Residential and Commercial Buildings
Easy applied torch on SBS waterproof membrane for residential and commercial buildings
Elastomeric waterproofing membrane produced from high quality bitumen mass, enriched with elastomers (SBS), reinforced with pad of polyester felt and protected on both sides with polyethylene burn-off film
It is an elastomeric waterproofing membrane produced from high quality bitumen mass, enriched with elastomers (SBS), reinforced with polyester felt or composite felt and protected on both sides with polyethylene burn-off film.
|Roll - length/width:||10 м² (10m x 1m .)|
|Flexibility at low temperature:||≤ - 20 ˚C|
|Resistance to high temperature:||≥ + 95˚C|
|Tensile strength – longitudinal/transversal:||800/500 -30 ( N/50mm)|
|Elongation at break - longitudinal/transversal:||40/40 ±5 %|
|Use:||Used for water protection in underground parts of buildings and for waterproofing of flat roofs|
|Application:||The membrane is applying by torching with 10 cm overlaps.|
Application substrate should be cleaned off loose piecs, oil and other chemicals. Surface defects are repaired, corners are chamfered with bitumen fillet tape. Recommended to use primer oil before the application of membrane to accomplish finish.
1.10 cm overlapping shall be allowed for joints and 15cm overlapping for ends by using welding torch.
2.The transverse joints of the first layer covering should be laid down in an offset position.
3.For the top layer, longitudinal and transverse joints of the first layer should be centered.
4.Roof covers should be laid perpendicular to the slope from the point where the slope is lowest.