|Type:||Waterproof Material||Main Material:||Asphalt, Polyester, Composite Felt|
|Thickness:||2mm, 3mm, 4mm,5mm||Length:||10m, 1m|
sbs modified bitumen membrane,
sbs modified bituminous membrane
Green Mineral Granule Coated SBS Modified Bitumen Waterproof Roofing Membrane
This product is a styrene-butadiene block copolymer (SBS), modified asphalt impregnated with a tire base, coated with an elastomeric asphalt coating on both sides, and sprinkled with fine sand, mineral particles (tablets) or coating on the upper surface. Waterproof membrane made of insulation material such as polyethylene film.
★ Strong impermeability
★ High tensile strength, large elongation, strong adaptability to shrinkage deformation and cracking of the base layer
★ Good low temperature performance, can still maintain its efficacy at -50 ℃, can be used in hot and cold areas, especially in cold areas
★ puncture resistance, puncture resistance, tear resistance
★ Corrosion resistance, mildew resistance, good weather resistance
★ Convenient construction, hot melt construction can be operated in all seasons, and the joints are reliable
Fiberglass SBS Modified Asphalt Waterproof Membrane
★ High tensile strength, good dimensional stability
★ Good high and low temperature resistance
★ Good resistance to damage, corrosion, mildew, and weather
★ Good construction performance and reliable seams
Waterproofing and moisture-proofing of roofs, walls, basements, toilets, etc. of key waterproofing projects and industrial and civil buildings; waterproofing of bridges, roads, parking lots, swimming pools, tunnels, cisterns and other buildings; especially suitable for frequent structural deformation and cold Buildings in the area; protection of pipes, anti-corrosion layers, and encapsulation and moisture protection.
|thickness||2mm, 3mm, 4mm|
|roll weight||28KG, 35KG, 45KG|
|roll coverage||15 m2, 10m2, 10m2|
|low temperature||-20degree, -10degree, -5degree|
|tensile strength||350N, 450N|
Application Key Points:
a) Baking the bonding surface of the molten coil with a hot-melt spray gun.
b) The coil and the substrate can be fully sticky, or sticky or sticky. The area is determined by the slope. When the minimum bonding is performed, the side of the roasted shale should be dried until the asphalt is melted and covered with shale pieces, and then dried. Bake the rolls that overlap. Should be baked and compacted. There must be excess bitumen extrusion at the overlap edges.
c) Long edge overlap, no less than 70mm for full sticking method, no less than 100 mm for empty paving, point sticking and strip sticking; short edge overlap, no less than 100mm for full sticking, empty paving, point sticking and stick sticking. Is not less than 150 mm. When adopting the double-layer method, the upper and lower layers of coils should be staggered by 1/3 or 1/2 widths with different seams.